AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar

Shop directly for high-quality AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar from the manufacturer. Custom orders available.
Request a Quote

PRODUCTS DETAILS

Basic Info.

Model NO.
4330V
Usage
Oil/Gas Drilling
Section Shape
Round
Transport Package
Anticorrosion Seaway Packages
Specification
OD 30-850mm
Trademark
SHUNFU
Origin
China
Production Capacity
100000 Tons Per Year

Product Description

AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar

Introduce
We are Chinese professional manufacturer of forged QT boring steel bar for oil services. We can supply multiple AISI/SAE standard alloy steel materials and forged bar diameter 80-500mm, boring hole diameter 10-250mm, max boring length 14 meters.  

Product advantage
Boring one side: no step in the boring bar
High-tech Boring Equipment: Good Straightness and Roughness, Tiny Tolerance and Roundness
Stable mechanical property in materials after QT process
Chemical component according to America standard 100%
Ensure UT and drift test for each pieces

Company advantage
We have decades of produce experience in QT/Boring process and strict quality management system(ISO NQA 9001)
We cooperated with several middle-east oil gas companies for many times and have API certificates.
Our sales team are professional steel industry staff and exporter with fluent English.
We accept variety convenient payment ways and the third parties inspection organization.

Specification
Product Name Forged QT Boring Alloy Steel Bar For Oil Services
Specification API 5CT/5CP/6A
Steel Grade 4130, 4140, 4145, 4145H, 4330V, 4137, 4340
Process Hot Forged+QT+Boring
Forged Bar Diameter 8-500mm
Boring Hole Diameter 10-250mm
Length Max14 meters
Inspection Size, Chemical, Mechanical, UT, Drift Test, Low/High Temp. Impact
Certificate MTC, CO/FE/FA, BV/SGS
MOQ 1-5 tons
Delivery Time 10-30 days
Trade Item FOB CIF CFR PPU PPD
Packaging Loose/Bundle/Wooden Pallet/Wooden Box/Plastic Cloth Wraps /Plastic End Caps/Beveled Protector

Introduce
AISI 4330V MOD is a modification of the 4330 alloy steel grade, with hardenability and other characteristics improved by the addition of vanadium. Alloy Steel 4330V offers good formability which is used for those that require a good combination of strength and impact resistance.

Applications
Shock loading or stress concentration applications are suited to this steel specification. 4330V is widely used in the oil and gas industry for applications such as oil tools, drill jars and shoes, tool holders and reamers and in the aerospace industry for applications such as bolting and air frames.

Standards
AMS 6427, AMS 6359, AMS 6304, ASTM A646, API 7 Specification

Chemicals Composition
Grade C Mn max Si max Cr Mo Ni P max S max V
4330V 0.2-0.30 1.0 0.80 0.40-0.60 0.30-0.50 1-1.5 0.025 0.010 0.05-0.10

Mechanical Properties
Yield strength Rp0.2,
MPa
Tensile strength Rm,
MPa
Elongation
[%]
Hardness
[HBW]
Impact, Charpy-V, -20ºC
[J]
 1034  1138  15  341-388  32

Heat Treatment
Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.

Annealing
Heat the steel slowly to 820-860°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 580°C followed by air cooling.

Stress Relieving
When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.

Hardening
4330V steel is usually supplied ready heat treated to 35-39 HRc. If further heat treatment is required annealed 4330V should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.

Tempering
Heat carefully to a suitable temperature selected by reference to a tempering chart or table, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air.

Forging
Preheat the steel carefully, then raise the temperature to 1070-1230°C for forging. Do not forge below 850°C. 4330V has good forging characteristics but care must be taken when cooling the steel due to its susceptibility to cracking. Cooling in ash or lime after forging is recommended.

Machining
Normalize and Temper at 1250°F(677°C) maximum prior to rough machine. This steel may also be machined at maximum strength, but machining must then be followed with a stress relieving at approximately 400°F(204°C).

Weldability
The steel has good welding characteristics and can be welded by resistance flash welding.

Mill′s test certificate
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar